Evaluación del incremento de polietilentereftalato amorfo obtenido por reciclaje mecánico al proceso de inyección y soplado de botellas no retornables en Iberplast S.A.S.

The physicochemical properties of polyethylene terephthalate in amorphous state, obtained from industrial surpluses, for the manufacture of non-returnable bottles were characterized. From the above, an intrinsic viscosity of 0.538 +/- 0.024 dL / g, acetaldehyde concentration of 4.00 +/- 2.00 ppm, de...

Full description

Autores:

Tipo de recurso:

Fecha de publicación:: 2020

Institución:: Universidad de América

Repositorio:: Lumieres

Idioma:: spa

id	Lumieres_c5db0bbf492aaa6e43a8fa55ef5f5c56
oai_identifier_str	oai:repository.uamerica.edu.co:20.500.11839/8112
network_acronym_str	Lumieres
network_name_str	Lumieres
repository_id_str
dc.title.none.fl_str_mv	Evaluación del incremento de polietilentereftalato amorfo obtenido por reciclaje mecánico al proceso de inyección y soplado de botellas no retornables en Iberplast S.A.S. Evaluation of the increase of amorphous polyethylenterephthalate obtained by mechanical recycling from the injection and blowing process of non.returnable bottles in Iberplast S.A.S.
title	Evaluación del incremento de polietilentereftalato amorfo obtenido por reciclaje mecánico al proceso de inyección y soplado de botellas no retornables en Iberplast S.A.S.
spellingShingle	Evaluación del incremento de polietilentereftalato amorfo obtenido por reciclaje mecánico al proceso de inyección y soplado de botellas no retornables en Iberplast S.A.S. Botellas no retornables Proceso de inyección Reciclaje mecánico Non-returnable bottles Injection process Mechanical recycling Tesis y disertaciones académicas
title_short	Evaluación del incremento de polietilentereftalato amorfo obtenido por reciclaje mecánico al proceso de inyección y soplado de botellas no retornables en Iberplast S.A.S.
title_full	Evaluación del incremento de polietilentereftalato amorfo obtenido por reciclaje mecánico al proceso de inyección y soplado de botellas no retornables en Iberplast S.A.S.
title_fullStr	Evaluación del incremento de polietilentereftalato amorfo obtenido por reciclaje mecánico al proceso de inyección y soplado de botellas no retornables en Iberplast S.A.S.
title_full_unstemmed	Evaluación del incremento de polietilentereftalato amorfo obtenido por reciclaje mecánico al proceso de inyección y soplado de botellas no retornables en Iberplast S.A.S.
title_sort	Evaluación del incremento de polietilentereftalato amorfo obtenido por reciclaje mecánico al proceso de inyección y soplado de botellas no retornables en Iberplast S.A.S.
dc.contributor.none.fl_str_mv	Moreno Torres, Edgar Fernando Lizarazo Castellanos, Jenny Marcela
dc.subject.none.fl_str_mv	Botellas no retornables Proceso de inyección Reciclaje mecánico Non-returnable bottles Injection process Mechanical recycling Tesis y disertaciones académicas
topic	Botellas no retornables Proceso de inyección Reciclaje mecánico Non-returnable bottles Injection process Mechanical recycling Tesis y disertaciones académicas
description	The physicochemical properties of polyethylene terephthalate in amorphous state, obtained from industrial surpluses, for the manufacture of non-returnable bottles were characterized. From the above, an intrinsic viscosity of 0.538 +/- 0.024 dL / g, acetaldehyde concentration of 4.00 +/- 2.00 ppm, density of 1.53 +/- 0.05 g / cm3 and melt index of 129 +/-22 g/10min was defined for pelleting. Second, the physicochemical and mechanical properties of preforms and non-returnable 2L bottles, manufactured with the current dosage of 3% PET in amorphous state, were determined. It was obtained 0.830 +/- 0.015 dL / g of intrinsic viscosity, 2.32 +/- 0.605 ppm of acetaldehyde concentration, resistance to vertical compression of 29.98 +/- 1.72 kg-F and, without failure of any bottle in the test of internal pressure resistance at 135 psi for 13 seconds.
publishDate	2020
dc.date.none.fl_str_mv	2020-08-10 2021-01-26T00:05:26Z 2021-01-26T00:05:26Z
dc.type.none.fl_str_mv	bachelorThesis
dc.type.coar.fl_str_mv	http://purl.org/coar/resource_type/c_7a1f
dc.identifier.none.fl_str_mv	APA 7th - Díaz Contreras, J. P. y Parra Landinez, P. A. (2020) Evaluación del incremento de polietilentereftalato amorfo obtenido por reciclaje mecánico al proceso de inyección y soplado de botellas no retornables en Iberplast S.A.S.. [Trabajo de grado, Fundación Universidad de América] Repositorio Institucional Lumieres. https://hdl.handle.net/20.500.11839/8112 https://hdl.handle.net/20.500.11839/8112
identifier_str_mv	APA 7th - Díaz Contreras, J. P. y Parra Landinez, P. A. (2020) Evaluación del incremento de polietilentereftalato amorfo obtenido por reciclaje mecánico al proceso de inyección y soplado de botellas no retornables en Iberplast S.A.S.. [Trabajo de grado, Fundación Universidad de América] Repositorio Institucional Lumieres. https://hdl.handle.net/20.500.11839/8112
url	https://hdl.handle.net/20.500.11839/8112
dc.language.iso.fl_str_mv	spa
language	spa
dc.rights.none.fl_str_mv	Atribución – No comercial http://purl.org/coar/access_right/c_abf2
rights_invalid_str_mv	Atribución – No comercial http://purl.org/coar/access_right/c_abf2
dc.format.none.fl_str_mv	application/pdf application/pdf
dc.publisher.none.fl_str_mv	Fundación Universidad de América
publisher.none.fl_str_mv	Fundación Universidad de América
institution	Universidad de América
repository.name.fl_str_mv
repository.mail.fl_str_mv
_version_	1841553086309466112
spelling	Evaluación del incremento de polietilentereftalato amorfo obtenido por reciclaje mecánico al proceso de inyección y soplado de botellas no retornables en Iberplast S.A.S.Evaluation of the increase of amorphous polyethylenterephthalate obtained by mechanical recycling from the injection and blowing process of non.returnable bottles in Iberplast S.A.S.Botellas no retornablesProceso de inyecciónReciclaje mecánicoNon-returnable bottlesInjection processMechanical recyclingTesis y disertaciones académicasThe physicochemical properties of polyethylene terephthalate in amorphous state, obtained from industrial surpluses, for the manufacture of non-returnable bottles were characterized. From the above, an intrinsic viscosity of 0.538 +/- 0.024 dL / g, acetaldehyde concentration of 4.00 +/- 2.00 ppm, density of 1.53 +/- 0.05 g / cm3 and melt index of 129 +/-22 g/10min was defined for pelleting. Second, the physicochemical and mechanical properties of preforms and non-returnable 2L bottles, manufactured with the current dosage of 3% PET in amorphous state, were determined. It was obtained 0.830 +/- 0.015 dL / g of intrinsic viscosity, 2.32 +/- 0.605 ppm of acetaldehyde concentration, resistance to vertical compression of 29.98 +/- 1.72 kg-F and, without failure of any bottle in the test of internal pressure resistance at 135 psi for 13 seconds.Se caracterizaron las propiedades fisicoquímicas del Polietilentereftalato en estado amorfo, obtenido de excedentes industriales, para la fabricación de botellas no retornables. De lo anterior, se definió para el peletizado una viscosidad intrínseca de 0.538 +/-0.024 dL/g, concentración de acetaldehído de 4.00+/-2.00 ppm, densidad de 1.53 +/-0.05 g/cm3 e índice de fluidez de 129 +/-22 g/10min. En segundo lugar, se determinaron las propiedades fisicoquímicas y mecánicas de preformas y botellas no retornables de 2L, fabricadas con la dosificación actual de 3% de PET en estado amorfo. Se obtuvo 0.830+/-0.015 dL/g de viscosidad intrínseca, 2.32 +/-0.605 ppm de concentración de acetaldehído, resistencia a la compresión vertical de 29.98 +/- 1.72 kg-F y, sin falla de ninguna botella en la prueba de resistencia a la presión interna a 135 psi durante 13 segundos.Fundación Universidad de AméricaMoreno Torres, Edgar FernandoLizarazo Castellanos, Jenny MarcelaDíaz Contreras, Jeimmy PaolaParra Landinez, Paula Alejandra2021-01-26T00:05:26Z2021-01-26T00:05:26Z2020-08-10bachelorThesishttp://purl.org/coar/resource_type/c_7a1fapplication/pdfapplication/pdfAPA 7th - Díaz Contreras, J. P. y Parra Landinez, P. A. (2020) Evaluación del incremento de polietilentereftalato amorfo obtenido por reciclaje mecánico al proceso de inyección y soplado de botellas no retornables en Iberplast S.A.S.. [Trabajo de grado, Fundación Universidad de América] Repositorio Institucional Lumieres. https://hdl.handle.net/20.500.11839/8112https://hdl.handle.net/20.500.11839/8112Atribución – No comercialYo (nosotros) en calidad de titular(es) de la obra, autorizo (autorizamos) al Sistema de Bibliotecas de la Fundación Universidad América para que incluya una copia, indexe y divulgue en el Repositorio Digital Institucional – Lumieres, la obra mencionada con el fin de facilitar los procesos de visibilidad e impacto de la misma, conforme a los derechos patrimoniales que me(nos) corresponde(n) y que incluyen: la reproducción, comunicación pública, distribución al público, transformación, en conformidad con la normatividad vigente sobre derechos de autor y derechos conexos (Ley 23 de 1982, Ley 44 de 1993, Decisión Andina 351 de 1993, entre otras). Al respecto como Autor(es) manifestamos conocer que: - La autorización es de carácter no exclusiva y limitada, esto implica que la licencia tiene una vigencia, que no es perpetua y que el autor puede publicar o difundir su obra en cualquier otro medio, así como llevar a cabo cualquier tipo de acción sobre el documento. - La autorización tendrá una vigencia de cinco años a partir del momento de la inclusión de la obra en el repositorio, prorrogable indefinidamente por el tiempo de duración de los derechos patrimoniales del autor y podrá darse por terminada una vez el autor lo manifieste por escrito a la institución, con la salvedad de que la obra es difundida globalmente y cosechada por diferentes buscadores y/o repositorios en Internet, lo que no garantiza que la obra pueda ser retirada de manera inmediata de otros sistemas de información en los que se haya indexado, diferentes al Repositorio Digital Institucional – Lumieres de la Fundación Universidad América. - La autorización de publicación comprende el formato original de la obra y todos los demás que se requiera, para su publicación en el repositorio. Igualmente, la autorización permite a la institución el cambio de soporte de la obra con fines de preservación (impreso, electrónico, digital, Internet, intranet, o cualquier otro formato conocido o por conocer). - La autorización es gratuita y se renuncia a recibir cualquier remuneración por los usos de la obra, de acuerdo con la licencia establecida en esta autorización. - Al firmar esta autorización, se manifiesta que la obra es original y no existe en ella ninguna violación a los derechos de autor de terceros. En caso de que el trabajo haya sido financiado por terceros, el o los autores asumen la responsabilidad del cumplimiento de los acuerdos establecidos sobre los derechos patrimoniales de la obra. - Frente a cualquier reclamación por terceros, el o los autores serán los responsables. En ningún caso la responsabilidad será asumida por la Fundación Universidad de América. - Con la autorización, la Universidad puede difundir la obra en índices, buscadores y otros sistemas de información que favorezcan su visibilidad.http://purl.org/coar/access_right/c_abf2spaoai:repository.uamerica.edu.co:20.500.11839/81122025-02-01T08:46:23Z

Evaluación del incremento de polietilentereftalato amorfo obtenido por reciclaje mecánico al proceso de inyección y soplado de botellas no retornables en Iberplast S.A.S.

Publicaciones similares