Efecto de la temperatura de revenido en la resistencia a la corrosión por picaduras y localizada de un acero inoxidable austenítico AISI304.

This thesis project investigates the effect of tempering temperature on the pitting and intergranular corrosion resistance of AISI 304 austenitic stainless steel. The steel was subjected to solution treatment at 1100°C and tempered at 500°C, 550°C, 600°C, 650°C, and 700°C, followed by potentiodynami...

Full description

Autores:

Tipo de recurso:

Fecha de publicación:: 2024

Institución:: Universidad de América

Repositorio:: Lumieres

Idioma:: spa

id	Lumieres_b94a6b8dc1001e086f48897ac7c290bb
oai_identifier_str	oai:repository.uamerica.edu.co:20.500.11839/9688
network_acronym_str	Lumieres
network_name_str	Lumieres
repository_id_str
dc.title.none.fl_str_mv	Efecto de la temperatura de revenido en la resistencia a la corrosión por picaduras y localizada de un acero inoxidable austenítico AISI304. Effect of tempering temperature on the pitting and localized corrosion resistance of AISI 304 austenitic stainless steel
title	Efecto de la temperatura de revenido en la resistencia a la corrosión por picaduras y localizada de un acero inoxidable austenítico AISI304.
spellingShingle	Efecto de la temperatura de revenido en la resistencia a la corrosión por picaduras y localizada de un acero inoxidable austenítico AISI304. Corrosión intergranular Corrosión por picadura Revenido Intergranular corrosion Pitting corrosion Tempered Tesis y disertaciones académicas
title_short	Efecto de la temperatura de revenido en la resistencia a la corrosión por picaduras y localizada de un acero inoxidable austenítico AISI304.
title_full	Efecto de la temperatura de revenido en la resistencia a la corrosión por picaduras y localizada de un acero inoxidable austenítico AISI304.
title_fullStr	Efecto de la temperatura de revenido en la resistencia a la corrosión por picaduras y localizada de un acero inoxidable austenítico AISI304.
title_full_unstemmed	Efecto de la temperatura de revenido en la resistencia a la corrosión por picaduras y localizada de un acero inoxidable austenítico AISI304.
title_sort	Efecto de la temperatura de revenido en la resistencia a la corrosión por picaduras y localizada de un acero inoxidable austenítico AISI304.
dc.contributor.none.fl_str_mv	Cárdenas Flechas, Leydi Julieta
dc.subject.none.fl_str_mv	Corrosión intergranular Corrosión por picadura Revenido Intergranular corrosion Pitting corrosion Tempered Tesis y disertaciones académicas
topic	Corrosión intergranular Corrosión por picadura Revenido Intergranular corrosion Pitting corrosion Tempered Tesis y disertaciones académicas
description	This thesis project investigates the effect of tempering temperature on the pitting and intergranular corrosion resistance of AISI 304 austenitic stainless steel. The steel was subjected to solution treatment at 1100°C and tempered at 500°C, 550°C, 600°C, 650°C, and 700°C, followed by potentiodynamic and cyclic polarization tests in 3.5% NaCl. The results showed that tempering temperature significantly impacts corrosion resistance: lower temperatures improved pitting resistance, while higher temperatures enhanced intergranular resistance due to the formation and distribution of chromium carbides. These findings are crucial for material selection in industrial applications requiring high corrosion resistance, optimizing heat treatment processes to improve the durability and reliability of components.
publishDate	2024
dc.date.none.fl_str_mv	2024-09-30T17:56:44Z 2024-09-30T17:56:44Z 2024-08-08
dc.type.none.fl_str_mv	bachelorThesis
dc.type.coar.fl_str_mv	http://purl.org/coar/resource_type/c_7a1f
dc.identifier.none.fl_str_mv	APA 7th - Pérez Valencia, M. Á. (2024) Efecto de la temperatura de revenido en la resistencia a la corrosión por picaduras y localizada de un acero inoxidable austenítico AISI304. [Trabajo de grado, Fundación Universidad de América] Repositorio Institucional Lumieres. https://hdl.handle.net/20.500.11839/9688 https://hdl.handle.net/20.500.11839/9688
identifier_str_mv	APA 7th - Pérez Valencia, M. Á. (2024) Efecto de la temperatura de revenido en la resistencia a la corrosión por picaduras y localizada de un acero inoxidable austenítico AISI304. [Trabajo de grado, Fundación Universidad de América] Repositorio Institucional Lumieres. https://hdl.handle.net/20.500.11839/9688
url	https://hdl.handle.net/20.500.11839/9688
dc.language.iso.fl_str_mv	spa
language	spa
dc.rights.none.fl_str_mv	Atribución – No comercial http://purl.org/coar/access_right/c_abf2
rights_invalid_str_mv	Atribución – No comercial http://purl.org/coar/access_right/c_abf2
dc.format.none.fl_str_mv	application/pdf application/pdf
dc.publisher.none.fl_str_mv	Fundación Universidad de América Tratamientos térmicos
publisher.none.fl_str_mv	Fundación Universidad de América Tratamientos térmicos
institution	Universidad de América
repository.name.fl_str_mv
repository.mail.fl_str_mv
_version_	1841553093337022464
spelling	Efecto de la temperatura de revenido en la resistencia a la corrosión por picaduras y localizada de un acero inoxidable austenítico AISI304.Effect of tempering temperature on the pitting and localized corrosion resistance of AISI 304 austenitic stainless steelCorrosión intergranularCorrosión por picaduraRevenidoIntergranular corrosionPitting corrosionTemperedTesis y disertaciones académicasThis thesis project investigates the effect of tempering temperature on the pitting and intergranular corrosion resistance of AISI 304 austenitic stainless steel. The steel was subjected to solution treatment at 1100°C and tempered at 500°C, 550°C, 600°C, 650°C, and 700°C, followed by potentiodynamic and cyclic polarization tests in 3.5% NaCl. The results showed that tempering temperature significantly impacts corrosion resistance: lower temperatures improved pitting resistance, while higher temperatures enhanced intergranular resistance due to the formation and distribution of chromium carbides. These findings are crucial for material selection in industrial applications requiring high corrosion resistance, optimizing heat treatment processes to improve the durability and reliability of components.Este proyecto de grado investiga el efecto de la temperatura de revenido en la resistencia a la corrosión por picaduras e intergranular de un acero inoxidable austenítico AISI 304. El acero fue sometido a solubilización a 1100°C y revenido a 500°C, 550°C, 600°C, 650°C y 700°C, seguido de pruebas potenciodinamicas y de polarización cíclica en NaCl al 3.5%. Los resultados mostraron que la temperatura de revenido impacta significativamente la resistencia a la corrosión: temperaturas más bajas mejoraron la resistencia a picaduras, mientras que temperaturas más altas mejoraron la resistencia intergranular debido a la formación y distribución de carburos de cromo. Estos hallazgos son cruciales para la selección de materiales en aplicaciones industriales que requieren alta resistencia a la corrosión, optimizando los procesos de tratamiento térmico para mejorar la durabilidad y fiabilidad de los componentes.Fundación Universidad de AméricaTratamientos térmicosCárdenas Flechas, Leydi JulietaPérez Valencia, Miguel Ángel2024-09-30T17:56:44Z2024-09-30T17:56:44Z2024-08-08bachelorThesishttp://purl.org/coar/resource_type/c_7a1fapplication/pdfapplication/pdfAPA 7th - Pérez Valencia, M. Á. (2024) Efecto de la temperatura de revenido en la resistencia a la corrosión por picaduras y localizada de un acero inoxidable austenítico AISI304. [Trabajo de grado, Fundación Universidad de América] Repositorio Institucional Lumieres. https://hdl.handle.net/20.500.11839/9688https://hdl.handle.net/20.500.11839/9688Atribución – No comercialYo (nosotros) en calidad de titular(es) de la obra, autorizo (autorizamos) al Sistema de Bibliotecas de la Fundación Universidad América para que incluya una copia, indexe y divulgue en el Repositorio Digital Institucional – Lumieres, la obra mencionada con el fin de facilitar los procesos de visibilidad e impacto de la misma, conforme a los derechos patrimoniales que me(nos) corresponde(n) y que incluyen: la reproducción, comunicación pública, distribución al público, transformación, en conformidad con la normatividad vigente sobre derechos de autor y derechos conexos (Ley 23 de 1982, Ley 44 de 1993, Decisión Andina 351 de 1993, entre otras). Al respecto como Autor(es) manifestamos conocer que: - La autorización es de carácter no exclusiva y limitada, esto implica que la licencia tiene una vigencia, que no es perpetua y que el autor puede publicar o difundir su obra en cualquier otro medio, así como llevar a cabo cualquier tipo de acción sobre el documento. - La autorización tendrá una vigencia de cinco años a partir del momento de la inclusión de la obra en el repositorio, prorrogable indefinidamente por el tiempo de duración de los derechos patrimoniales del autor y podrá darse por terminada una vez el autor lo manifieste por escrito a la institución, con la salvedad de que la obra es difundida globalmente y cosechada por diferentes buscadores y/o repositorios en Internet, lo que no garantiza que la obra pueda ser retirada de manera inmediata de otros sistemas de información en los que se haya indexado, diferentes al Repositorio Digital Institucional – Lumieres de la Fundación Universidad América. - La autorización de publicación comprende el formato original de la obra y todos los demás que se requiera, para su publicación en el repositorio. Igualmente, la autorización permite a la institución el cambio de soporte de la obra con fines de preservación (impreso, electrónico, digital, Internet, intranet, o cualquier otro formato conocido o por conocer). - La autorización es gratuita y se renuncia a recibir cualquier remuneración por los usos de la obra, de acuerdo con la licencia establecida en esta autorización. - Al firmar esta autorización, se manifiesta que la obra es original y no existe en ella ninguna violación a los derechos de autor de terceros. En caso de que el trabajo haya sido financiado por terceros, el o los autores asumen la responsabilidad del cumplimiento de los acuerdos establecidos sobre los derechos patrimoniales de la obra. - Frente a cualquier reclamación por terceros, el o los autores serán los responsables. En ningún caso la responsabilidad será asumida por la Fundación Universidad de América. - Con la autorización, la Universidad puede difundir la obra en índices, buscadores y otros sistemas de información que favorezcan su visibilidad.http://purl.org/coar/access_right/c_abf2spaoai:repository.uamerica.edu.co:20.500.11839/96882025-02-01T09:17:30Z

Efecto de la temperatura de revenido en la resistencia a la corrosión por picaduras y localizada de un acero inoxidable austenítico AISI304.

Publicaciones similares